Concrete Anchoring Chemical Epoxy Injection Type

SKU :

Product Description

Concrete EPOXY RESIN ANCHOR INJECTABLE is a multi-purpose, two components, high strength,

high modulus moisture-tolerant adhesive. with high quality plastic tube.

 

For more info please visit

https://eaglebondfastener.com/ab500

Application

1. For fixing machines, handrails, steel constructions, wooden constructions, reinforcement bars,

especially suitable for big diameter rebar and rods.

2. Bonding threaded rod and reinforcing bar into hardened concrete.
3. Suitable to resist loads in cracked or uncracked concrete base material for cases where anchor design theory and criteria applies.
4. Can be installed in a wide range of base material temperatures
5. Medium & Heavy-duty load applications.
6. High durability.
7. Ideal for indoor usage.

 

Technical Data Sheet

• Viscosity of Mixture:18-22Pa•S
• Splitting tensile strength ≥8.5MPa
• Bending strength ≥50MPa
• Compressive strength ≥60MPa
• Thixotopy index ≥4.0
• Distortion temperature ≥65℃
• Steel-steel tensile shear strength ≥16MPa
• C30,φ25, L=150mm condition tensile strength ≥11MPa
• C30,φ25, L=125mm condition bonding strength ≥17MPa
• Steel-steel T impact stripping length ≤25mm

 

 

Fixing Per Cartridge

Anchor Size	Hole Diameter(mm)	Hole Depth (mm)	Number of Fixings
M8	10	80	80
M10	13	90	42
M12	16	120	21
M16	20	145	11
M20	25	170	6
M24	28	210	4
M30	35	270	2
M36	40	330	1

 

TECHNICAL DATA SHEET

 

Product Performance

	Standard Requirement	Product Data
Splitting tensile strength	≥8.5 Mpa	8.85 Mpa
Bending strength	≥50 Mpa	52.1 Mpa without breakage
Compressive strength	≥60MPa	67.9MPa
Standard values of tensile strength of steel	≥10MPa	13.1MPa
Bond strength between ribbed steel bars and concrete under constrained drawing conditions C30 / φ25 / L=150m	≥10MPa	12.0MPa
Impact peeling length of steel	≤25mm	6.8mm
Thermal deformation temperature	≥65℃	67.91 ℃
Nonvolatile content(solid content)	≥99%	99.30%
Benzene/ (g/Kg)	≤5.0	0
Toluene + xylene/(g/Kg)	≤150	0.4
Halogenated hydrocarbon dichloromethane/(g/kg)	≤50	0
Halogenated hydrocarbon 1.2-two chloroethane(g/kg)	≤50	0
Halogenated hydrocarbon 1.1.2-three chloroethylhospital(g/kg)	≤50	0
Halogenated hydrocarbon Three chloroethane(g/kg)	≤50	0
Total volaile organic compounds(g/L)	≤700	22
Resistance to heat and heat aging (90d）	The shear strength reduction rate is compared with the short term test results at room temperature <12%	7.10%