TEDUN EPOXY RESIN ANCHOR INJECTABLE is a multi-purpose, two components, high strength,

high modulus moisture-tolerant adhesive. with high quality plastic tube.

 

Application

  1. For fixing machines, handrails, steel constructions, wooden constructions, reinforcement bars,

especially suitable for big diameter rebar and rods.

  1. Bonding threaded rod and reinforcing bar into hardened concrete.
  2. Suitable to resist loads in cracked or uncracked concrete base material for cases where anchor design theory and criteria applies.
  3. Can be installed in a wide range of base material temperatures
  4. Medium & Heavy-duty load applications.
  5. High durability.
  6. Ideal for indoor usage.

 

Technical Data Sheet

  • Viscosity of Mixture:18-22Pa•S
  • Splitting tensile strength ≥8.5MPa
  • Bending strength ≥50MPa
  • Compressive strength ≥60MPa
  • Thixotopy index ≥4.0
  • Distortion temperature ≥65℃
  • Steel-steel tensile shear strength ≥16MPa
  • C30,φ25, L=150mm condition tensile strength ≥11MPa
  • C30,φ25, L=125mm condition bonding strength ≥17MPa
  • Steel-steel T impact stripping length ≤25mm

 

 

Fixing Per Cartridge

Anchor Size

Hole

Diameter(mm)

Hole Depth

(mm)

Number of Fixings

 

M8

10

80

80

M10

13

90

42

M12

16

120

21

M16

20

145

11

M20

25

170

6

M24

28

210

4

M30

35

270

2

M36

40

330

1

 

TECHNICAL DATA SHEET

 

Product Performance

 

Standard Requirement

Product Data

Splitting tensile strength

≥8.5 Mpa

8.85 Mpa

Bending strength

≥50 Mpa

 

52.1 Mpa

without breakage

Compressive strength

≥60MPa

67.9MPa

Standard values of tensile strength of steel

≥10MPa

13.1MPa

Bond strength between ribbed steel bars and concrete under constrained drawing conditions

C30 / φ25 / L=150m

 

≥10MPa

12.0MPa

Impact peeling length of steel

≤25mm

6.8mm

Thermal deformation temperature

≥65℃

67.91 ℃

Nonvolatile content(solid content)

≥99%

99.30%

Benzene/ (g/Kg)

≤5.0

0

Toluene + xylene/(g/Kg)

≤150

0.4

Halogenated hydrocarbon

dichloromethane/(g/kg)

≤50

0

Halogenated hydrocarbon

1.2-two chloroethane(g/kg)

≤50

0

Halogenated hydrocarbon

1.1.2-three chloroethylhospital(g/kg)

≤50

0

Halogenated hydrocarbon

Three chloroethane(g/kg)

≤50

0

Total volaile organic compounds(g/L)

≤700

22

Resistance to heat and heat aging (90d)

The shear strength reduction

rate is compared with the

short term test results at room

temperature <12%

7.10%

 

Curing Time

Substrate temperature (℃)

-5

0

5

20

30

40

Installation Time (min)

70

60

45

25

20

8

Dry time (h) Curing time (h)

36

24

18

8

5

3

Curing time (h)

72

48

48

16

8

8

 

 

 